Smooth-Cast™ ONYX™

OnyxFastpint ⓘ F8AB7487-AEC7-4549-BDDD-37609C6C69D4
Polyurethane Resin
Size
1 kg 7.48 kg
Custom Property
fast slow

ultra-black, fast-curing, resin with superior physical properties and high heat resistance. A good choice for fast cold-cast bronze, brass, copper, nickel/silver, etc. effects.

  • Shore Hardness: 80D
  • Working time: 2.5 minutes
  • Demold time: 15 minutes
  • Mercury-free
  • Polishable finish
exclamation.svg health-hazard.svg

Danger

H315 - Causes skin irritation.
H317 - May cause an allergic skin reaction.
H320 -
H332 - Harmful if inhaled.
H334 - May cause allergy or asthma symptoms or breathing difficulties if inhaled.
€ 33.52

(€ 27.70 without 21% VAT)

In stock

Description

This resin offers a short working time of 2.5 minutes and a cure time of 10-15 minutes, making it suitable for creating cold cast metal effects like bronze, brass, copper, and nickel/silver.

Features

  • Ultra-black color, darker than other black resins
  • Can be polished and buffed to a high gloss shine
  • Higher heat resistance compared to other black resins
  • Mercury-free composition
  • Cost-effective compared to other black resins

Shore Hardness: 80D

Working time: 2.5 minutes

Demold Time: 15 minutes

Instructions

  • Measure equal parts of the resin components and mix thoroughly, ensuring to scrape the sides and bottom for a uniform blend. 
  • Work quickly due to the 2.5-minute working time:. 
  • Pour immediately into your mold. 
  • Allow the material to cure undisturbed. 
  • it can be demolded in about 10–15 minutes. 
  • For best results, post-cure at room temperature before sanding, polishing, or buffing to achieve a high-gloss, metallic finish. 
  • Ensure proper ventilation and wear protective gloves during use.

Available in Polyurethane Resin
Product Handling Time Cure Time Specific Gravity Specific Volume Shrinkage Mixed Viscocity Mix Ratio By Volume Pot Life Shore D Hardness Color Mixed Viscocity Cure Time Pot Life Specific Volume Specific Gravity Shrinkage Mix Ratio By Volume Shore D Hardness Handling Time Tensile Modulus Compressive Strength Compressive Modulus Flexural Strength Heat Deflection Temp Elongation At Break Ultimate Tensile Flexural Modulus Flexural Strength Flexural Modulus Ultimate Tensile Elongation At Break Heat Deflection Temp Compressive Strength Tensile Modulus Compressive Modulus Mix Ratio By Weight Mix Ratio By Weight
SMASH! Plastic™ 90 min. 16 h. 1.036 g/cc 26.7 cu. in./lb. 0.0001 in. / in. 900 cps 1A:1B 5 min. 80 Clear 900 cps 16 h. 5 min. 26.7 cu. in./lb. 1.036 g/cc 0.0001 in. / in. 1A:1B 80 90 min. - - - - - - - - - - - - - - - - - -
Feather Lite™ - 2 h. 0.67 g/cc 41.3 cu. in./lb. 0.003 in. / in. 410 cps 1A:1B 8.5 min. 58 Beige 410 cps 2 h. 8.5 min. 41.3 cu. in./lb. 0.67 g/cc 0.003 in. / in. 1A:1B 58 - 156,000 psi 3,070 psi 53,700 psi 3,440 psi 140 °F 1.6 % 2,160 psi 164,300 psi 3,440 psi 164,300 psi 2,160 psi 1.6 % 140 °F 3,070 psi 156,000 psi 53,700 psi - -
Plasti-Paste™ II 90 min. 24 h. 1.0 g/cc 27.73 cu. in./lb. 0.005 in. / in. Paste 1A:2B 10 min. 70 Off White Paste 24 h. 10 min. 27.73 cu. in./lb. 1.0 g/cc 0.005 in. / in. 1A:2B 70 90 min. 235,000 psi 4,980 psi 62,700 psi 3,840 psi 130 °F 1.14 % 2,150 psi 203,000 psi 3,840 psi 203,000 psi 2,150 psi 1.14 % 130 °F 4,980 psi 235,000 psi 62,700 psi 62A:100B 62A:100B
Axsson - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - -
Smooth-Cast™ ONYX™ - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - -

Why buy at FormX?

Subscribe to our Newsletter

Receive €5,- discount on your first purchase!

Visa logo iDeal logo Mastercard logo Paypal logo FedEx logo FedEx logo
This website has been developed by Usecue B.V.
© 2026 FormX B.V.