Tin-cured mold-making silicone for durable molds with excellent detail reproduction.

Shore Hardness: 30 A
Mix Ratio: 100A:10B by weight
Pot Life: 45 min, Cure Time: 24 hrs
Applicable temperature range: -54°C to 204°C (cured product)
Mixed Viscosity: 25,000 cps

€ 647.82

(€ 535.39 without 21% VAT)

In stock

Description

This tin-cured silicone rubber compound is known for its exceptional working properties and long library life.

Mold Max™ 30 features an exclusive catalyst and can be pigmented with silicone colorants.

Working time for these pourable silicones is 45 minutes, and they cure overnight at room temperature.

Vacuum degassing is recommended to remove entrapped air.

Features

Reproduces the finest detail.
Suitable for industrial and art applications, including molds for prototypes, furniture, sculpture, and architectural elements.
Can be thickened for brush-on applications.
Can cast materials such as wax, gypsum, low melt alloys/metals, and urethane, epoxy, or polyester resins without a release agent.

Technical Properties

Mix Ratio: 100A:10B by weight
Working time: 45 minutes
Cure Time: 24 hours
Shore Hardness: 30 A
Specific Gravity: 1.18 g/cc
Specific Volume: 0.85 cm³/g
Color: Pink
Tensile Strength: 3.98 MPa
100% Modulus: 758 kPa
Elongation @ Break: 300%
Die B Tear Strength: 21.9 kN/m
Useful Temperature Range: -54°C to 204°C
Volume Resistance: 8.29E+11 ohm
Volume Resistivity: 5.83E+13 ohm/cm
Dielectric Constant, 100Hz: 3.29
Dielectric Strength: 330 volts/mil
Dissipation Factor, 100Hz: 0.005
Shrinkage: 0.002 mm/mm
Mixed Viscosity: 25,000 cps

Instructions

Safety

Use in a properly ventilated area.
Wear safety glasses, long sleeves, and rubber gloves (vinyl gloves only).
Store and use material at room temperature (23°C).

Measuring & Mixing

Pre-mix Part B thoroughly.
Weigh Part A & B using a gram scale.
Mix for 3 minutes, scraping sides and bottom.
Vacuum degassing is recommended.

Pouring / Curing / Post Curing

Pour mixture in a single spot at the lowest point.
Allow mold to cure overnight (at least 16 hrs) at room temperature.
Post cure for 4 hours at 65°C if necessary.

Thickening for Brush-on Application

Use a thickener for vertical surfaces.
Apply a thin coat, wait for tackiness, then apply the next coat.
Final mold thickness should be at least 1 cm (3/8 in).

Accelerating Cure Time

Use an accelerator to reduce demold time to as little as 30 minutes.

Thinning

Use a thinner to lower viscosity and increase pot life.

Mold Performance & Storage

Clean mold with soap solution before storage.
Store on a level surface in a cool, dry environment.

Specifications

Hundred Percent Modulus	110 psi
Color	Pink
Die B Tear Strength	125 pli
Mixed Viscocity	25,000 cps
Useful Temperature Min	-65 °F
Cure Time	24 hours
Pot Life	45 minutes
Specific Volume	23.5 cu. in./lb.
Specific Gravity	1.18 g/cc
Mix Ratio By Weight	100A:10B
Shrinkage	0.002 in. / in.
Dielectric Strength	330 volts/mil
Tensile Strength	577 psi
Elongation At Break	300 %
Dielectric Constant 100hz	3.290000
Shore A Hardness	30
Volume Resistivity	5.83E+13 ohm/cm
Dissipation Factor 100hz	0.005000
Volume Resistance	8.29E+11 ohm

Available in Tin Cure Silicone

Product	Cure Time	Shore A Hardness	Specific Gravity	Specific Volume	Tensile Strength	Shrinkage	Elongation At Break	Hundred Percent Modulus	Die B Tear Strength	Useful Temperature Min	Dielectric Strength	Dielectric Constant 100hz	Dissipation Factor 100hz	Volume Resistivity	Volume Resistance	Mixed Viscocity	Mix Ratio By Weight	Pot Life	Hundred Percent Modulus	Color	Die B Tear Strength	Mixed Viscocity	Useful Temperature Min	Cure Time	Pot Life	Specific Volume	Specific Gravity	Mix Ratio By Weight	Shrinkage	Dielectric Strength	Tensile Strength	Elongation At Break	Dielectric Constant 100hz	Shore A Hardness	Volume Resistivity	Dissipation Factor 100hz	Volume Resistance	Thermal Conductivity	Thermal Conductivity
Mold Max™ 25	24 h.	25	1.18 g/cc	23.5 cu. in./lb.	577 psi	0.001 in. / in.	375 %	80 psi	130 pli	-65 °F	330 volts/mil	3.29	0.005	5.83E+13 ohm/cm	8.29E+11 ohm	25,000 cps	100A:5B	60 min.	80 psi	Purple	130 pli	25,000 cps	-65 °F	24 h.	60 min.	23.5 cu. in./lb.	1.18 g/cc	100A:5B	0.001 in. / in.	330 volts/mil	577 psi	375 %	3.290000	25	5.83E+13 ohm/cm	0.005000	8.29E+11 ohm	-	-
Mold Max™ 60	24 h.	60	1.45 g/cc	19.1 cu. in./lb.	398 psi	0.0015 in. / in.	132 %	331 psi	63 pli	-65 °F	>500 volts/mil	3.4	0.02	9.000000E+14 ohm/cm	-	20,000 cps	100A:3B	40 min.	331 psi	Red	63 pli	20,000 cps	-65 °F	24 h.	40 min.	19.1 cu. in./lb.	1.45 g/cc	100A:3B	0.0015 in. / in.	>500 volts/mil	398 psi	132 %	3.400000	60	9.000000E+14 ohm/cm	0.020000	-	0.347 W/M*K	0.347 W/M*K
Mold Max™ 20	24 h.	20	1.18 g/cc	23.5 cu. in./lb.	555 psi	0.001 in. / in.	512 %	49 psi	110 pli	-65 °F	330 volts/mil	3.29	0.005	5.83E+13 ohm/cm	8.29E+11 ohm	25,000 cps	100A:10B	45 min.	49 psi	Light Pink	110 pli	25,000 cps	-65 °F	24 h.	45 min.	23.5 cu. in./lb.	1.18 g/cc	100A:10B	0.001 in. / in.	330 volts/mil	555 psi	512 %	3.290000	20	5.83E+13 ohm/cm	0.005000	8.29E+11 ohm	-	-
Mold Max™ 30	24 h.	30	1.18 g/cc	23.5 cu. in./lb.	577 psi	0.002 in. / in.	300 %	110 psi	125 pli	-65 °F	330 volts/mil	3.29	0.005	5.83E+13 ohm/cm	8.29E+11 ohm	25,000 cps	100A:10B	45 min.	110 psi	Pink	125 pli	25,000 cps	-65 °F	24 h.	45 min.	23.5 cu. in./lb.	1.18 g/cc	100A:10B	0.002 in. / in.	330 volts/mil	577 psi	300 %	3.290000	30	5.83E+13 ohm/cm	0.005000	8.29E+11 ohm	-	-
Mold Max™ 10	24 h.	10	1.15 g/cc	24.1 cu. in./lb.	473 psi	0.001 in. / in.	529 %	35 psi	100 pli	-65 °F	330 volts/mil	3.29	0.005	5.83E+13 ohm/cm	8.29E+11 ohm	15,000 cps	100A:10B	45 min.	35 psi	Light Pink	100 pli	15,000 cps	-65 °F	24 h.	45 min.	24.1 cu. in./lb.	1.15 g/cc	100A:10B	0.001 in. / in.	330 volts/mil	473 psi	529 %	3.290000	10	5.83E+13 ohm/cm	0.005000	8.29E+11 ohm	-	-
Mold Max™ 40	24 h.	40	1.14 g/cc	24.3 cu. in./lb.	550 psi	0.004 in. / in.	250 %	190 psi	120 pli	-65 °F	330 volts/mil	3.29	0.005	5.83E+13 ohm/cm	8.29E+11 ohm	45,000 cps	100A:10B	45 min.	190 psi	Mint Green	120 pli	45,000 cps	-65 °F	24 h.	45 min.	24.3 cu. in./lb.	1.14 g/cc	100A:10B	0.004 in. / in.	330 volts/mil	550 psi	250 %	3.290000	40	5.83E+13 ohm/cm	0.005000	8.29E+11 ohm	-	-

Mold Max™ 30