TASK™ 4

Task4x ⓘ E9D24C9F-33C3-D540-86E4-34AEE546880C
Polyurethane Resin

Ultra-thin-section polyurethane casting resin featuring low shrinkage and excellent detail capture.

  • Shore Hardness: 83D
  • Mix Ratio: 1:1 by weight
  • Working time: 20 min
  • Cure Time: 16 hrs
  • Tensile Strength: 44.8 MPa
exclamation.svg health-hazard.svg

Danger

H315 - Causes skin irritation.
H317 - May cause an allergic skin reaction.
H320 -
H332 - Harmful if inhaled.
H334 - May cause allergy or asthma symptoms or breathing difficulties if inhaled.
€ 177.40

(€ 146.61 without 21% VAT)

Out of stock

Description

This polyurethane casting resin is designed for strength in ultra-thin sections from 0.75 mm to 1.27 cm (0.03” to 0.50”). TASK™ 4 features low mixed viscosity for capturing fine details and exhibits minimal shrinkage, making it ideal for prototypes and design models. 

The working time is 20 minutes, and it cures in 16 hours at 23°C.

Color customization is possible with SO-Strong™ tints. Fully cured models are tough, durable, machinable, and paintable, resisting moisture and mild solvents. 

Applications include prototype models, toys, miniatures, mechanical parts, and props.

Technical Properties

  • Mix Ratio By Weight: 100A:100B
  • Working time: 20 minutes
  • Cure Time: 16 hours
  • Shore Hardness: 83 D
  • Specific Gravity: 1.167 g/cc
  • Specific Volume: 0.86 cm³/g
  • Color: Ivory
  • Elongation@Break: 4%
  • Tensile Strength: 44.8 MPa
  • Tensile Modulus: 896 kPa
  • Flexural Strength: 62.1 MPa
  • Flexural Modulus: 1,407 kPa
  • Compressive Strength: 51 MPa
  • Heat Deflection Temp: 43°C
  • Compressive Modulus: 517 kPa
  • Shrinkage: 0.0035 mm/mm
  • Mixed Viscosity: 250 mPa·s

Instructions

Storage and Handling

Store and use materials in a warm environment at 23°C. The product is moisture-sensitive and should be used promptly. Use clean metal, glass, or plastic tools and containers for mixing. Ensure good ventilation and wear safety gear, including glasses, long sleeves, and rubber gloves.

Release Agent Application

Apply a release agent to all surfaces in contact with the plastic. Use a mold-specific release agent like Universal™ Mold Release.

Brush the release agent over surfaces, apply a light mist, and let it dry for 30 minutes.

Measuring and Mixing

Mix in a 100A:100B weight ratio using an accurate scale. Stir Part A and Part B before combining. Mix thoroughly, scraping the container's sides and bottom. Add tints or pigments to Part B before mixing with Part A.

Replace lids immediately after use to prolong shelf life. 

Use XTEND-IT™ Dry Gas Blanket to extend the shelf life of unused products.

Pouring

Pour the mixture at the mold's lowest point. Avoid pouring directly over objects if encapsulating. Use pressure casting at 4.2 kg/cm² for best results.

Curing

Ensure adequate ventilation during use. Allow castings to cool to room temperature before handling. Demold time varies with mass and configuration. For rotational or hollow castings, backfill with rigid foam for reinforcement.

Post Curing

Post curing accelerates full cure and enhances properties. Cure at room temperature, then heat at 65°C for 4 hours. Allow to cool before handling.

Performance

Cured castings are rigid, durable, and resistant to moisture, heat, and solvents. They can be machined, painted, or bonded after removing any release agent. Suitable for outdoor display after priming and painting.

Specifications

Color Ivory
Mixed Viscocity 250 cps
Cure Time 16 hours
Pot Life 20 minutes
Flexural Strength 9,000 psi
Flexural Modulus 204,000 psi
Specific Volume 23.9 cu. in./lb.
Specific Gravity 1.167 g/cc
Mix Ratio By Weight 100A:100B
Shrinkage 0.0035 in. / in.
Tensile Strength 6,500 psi
Elongation At Break 4 %
Shore D Hardness 83
Heat Deflection Temp 110 °F
Compressive Strength 7,400 psi
Tensile Modulus 130,000 psi
Compressive Modulus 75,000 psi
Available in Polyurethane Resin
Product Cure Time Specific Gravity Specific Volume Tensile Strength Tensile Modulus Compressive Strength Compressive Modulus Flexural Strength Shrinkage Heat Deflection Temp Elongation At Break Flexural Modulus Mixed Viscocity Mix Ratio By Volume Mix Ratio By Weight Pot Life Shore D Hardness Color Mixed Viscocity Cure Time Pot Life Flexural Strength Flexural Modulus Specific Volume Specific Gravity Mix Ratio By Weight Shrinkage Mix Ratio By Volume Tensile Strength Elongation At Break Shore D Hardness Heat Deflection Temp Compressive Strength Tensile Modulus Compressive Modulus Handling Time Handling Time Heat Deflection With Post Cure Heat Deflection With Post Cure Shore A Hardness Die C Tear Strength Hundred Percent Modulus Hundred Percent Modulus Die C Tear Strength Shore A Hardness
TASK™ 2 60 min. 1.12 g/cc 24.7 cu. in./lb. 6,650 psi 290,000 psi 8,300 psi 78,000 psi 9,500 psi 0.005 in. / in. 134 °F 6 % 288,000 psi 150 cps 1A:1B 115A:100B 7 min. 80 White 150 cps 60 min. 7 min. 9,500 psi 288,000 psi 24.7 cu. in./lb. 1.12 g/cc 115A:100B 0.005 in. / in. 1A:1B 6,650 psi 6 % 80 134 °F 8,300 psi 290,000 psi 78,000 psi - - - - - - - - - -
TASK™ 3 90 min. 1.12 g/cc 24.7 cu. in./lb. 6,650 psi 290,000 psi 8,300 psi 78,000 psi 9,500 psi 0.0025 in. / in. 134 °F 6 % 288,000 psi 150 cps 1A:1B 115A:100B 20 min. 80 White 150 cps 90 min. 20 min. 9,500 psi 288,000 psi 24.7 cu. in./lb. 1.12 g/cc 115A:100B 0.0025 in. / in. 1A:1B 6,650 psi 6 % 80 134 °F 8,300 psi 290,000 psi 78,000 psi - - - - - - - - - -
TASK™ 4 16 h. 1.167 g/cc 23.9 cu. in./lb. 6,500 psi 130,000 psi 7,400 psi 75,000 psi 9,000 psi 0.0035 in. / in. 110 °F 4 % 204,000 psi 250 cps - 100A:100B 20 min. 83 Ivory 250 cps 16 h. 20 min. 9,000 psi 204,000 psi 23.9 cu. in./lb. 1.167 g/cc 100A:100B 0.0035 in. / in. - 6,500 psi 4 % 83 110 °F 7,400 psi 130,000 psi 75,000 psi - - - - - - - - - -
TASK™ 5 24 h. 1.1 g/cc 25.2 cu. in./lb. 4,530 psi 200,000 psi 6,700 psi 83,000 psi 6,480 psi 0.007 in. / in. 145 °F 5 % 216,000 psi 600 cps 1A:1B 1A:1B 3 min. 77 Tan 600 cps 24 h. 3 min. 6,480 psi 216,000 psi 25.2 cu. in./lb. 1.1 g/cc 1A:1B 0.007 in. / in. 1A:1B 4,530 psi 5 % 77 145 °F 6,700 psi 200,000 psi 83,000 psi 15 min. 15 min. - - - - - - - -
TASK™ 6 24 h. 1.07 g/cc 25.9 cu. in./lb. 5,200 psi 146,000 psi 5,570 psi 65,000 psi 6,200 psi 0.0031 in. / in. 162 °F 4 % 182,500 psi 800 cps 1A:1B 1A:1B 7 min. 75 Tan 800 cps 24 h. 7 min. 6,200 psi 182,500 psi 25.9 cu. in./lb. 1.07 g/cc 1A:1B 0.0031 in. / in. 1A:1B 5,200 psi 4 % 75 162 °F 5,570 psi 146,000 psi 65,000 psi 75 min. 75 min. - - - - - - - -
TASK™ 7 10 min. 1.2 g/cc 23.1 cu. in./lb. 3,390 psi 150,700 psi 5,140 psi 57,600 psi 5,450 psi 0.0111 in. / in. 131 °F 15.1 % 148,900 psi 200 cps 1A:1B 104A:100B 2.5 min. 73 Off-White 200 cps 10 min. 2.5 min. 5,450 psi 148,900 psi 23.1 cu. in./lb. 1.2 g/cc 104A:100B 0.0111 in. / in. 1A:1B 3,390 psi 15.1 % 73 131 °F 5,140 psi 150,700 psi 57,600 psi - - - - - - - - - -
TASK™ 8 15 min. 1.09 g/cc 25.4 cu. in./lb. 5,840 psi 246,000 psi 8,760 psi 77,400 psi 8,280 psi 0.01 in. / in. 194 °F 4 % 271,000 psi 100 cps 1A:1B 120A:100B 2.5 min. 80 Off-White 100 cps 15 min. 2.5 min. 8,280 psi 271,000 psi 25.4 cu. in./lb. 1.09 g/cc 120A:100B 0.01 in. / in. 1A:1B 5,840 psi 4 % 80 194 °F 8,760 psi 246,000 psi 77,400 psi - - 263 °F 263 °F - - - - - -
TASK™ 11 16 h. 1.12 g/cc 24.7 cu. in./lb. 2,500 psi - - - - 0.0024 in. / in. - 100 % - 2,000 cps - 100A:100B 20 min. 60 Translucent White 2,000 cps 16 h. 20 min. - - 24.7 cu. in./lb. 1.12 g/cc 100A:100B 0.0024 in. / in. - 2,500 psi 100 % 60 - - - - - - - - - - - - - -
TASK™ 12 16 h. 1.08 g/cc 26 cu. in./lb. 2,700 psi - - - - 0.001 in. / in. - 300 % - 2,400 cps - 100A:44B 20 min. 60 Clear Amber 2,400 cps 16 h. 20 min. - - 26 cu. in./lb. 1.08 g/cc 100A:44B 0.001 in. / in. - 2,700 psi 300 % 60 - - - - - - - - - - - - - -
TASK™ 13 20 min. 1.15 g/cc 24.1 cu. in./lb. 1,800 psi - - - - 0.005 in. / in. - 125 % - 800 cps - 100A:120B 3 min. 50 Black 800 cps 20 min. 3 min. - - 24.1 cu. in./lb. 1.15 g/cc 100A:120B 0.005 in. / in. - 1,800 psi 125 % 50 - - - - - - - - - - - - - -
TASK™ 14 45 min. 1.15 g/cc 24.1 cu. in./lb. 1,800 psi - - - - 0.0035 in. / in. - 125 % - 800 cps - 100A:120B 10 min. 50 Black 800 cps 45 min. 10 min. - - 24.1 cu. in./lb. 1.15 g/cc 100A:120B 0.0035 in. / in. - 1,800 psi 125 % 50 - - - - - - - - - - - - - -
TASK™ 15 1 h. 1.12 g/cc 24.7 cu. in./lb. 2,720 psi 126,000 psi 5,450 psi 60,000 psi 5,450 psi 0.0042 in. / in. 117 °F 20 % 170,000 psi 600 cps - 75A:100B 6 min. 75 Opaque White 600 cps 1 h. 6 min. 5,450 psi 170,000 psi 24.7 cu. in./lb. 1.12 g/cc 75A:100B 0.0042 in. / in. - 2,720 psi 20 % 75 117 °F 5,450 psi 126,000 psi 60,000 psi - - - - - - - - - -
TASK™ 16 24 h. 1.08 g/cc 25.64 cu. in./lb. 2,264 psi - - - - 0.0025 in. / in. - 233 % - 1,400 cps - 1A:2B 6 min. 30 Light Yellow 1,400 cps 24 h. 6 min. - - 25.64 cu. in./lb. 1.08 g/cc 1A:2B 0.0025 in. / in. - 2,264 psi 233 % 30 - - - - 90 min. 90 min. - - 80 197 pli 855 psi 855 psi 197 pli 80
TASK™ 18 16 h. 1.57 g/cc 17.6 cu. in./lb. 3,250 psi 514,000 psi 8,420 psi 97,300 psi 10,700 psi 0.0006 in. / in. 149 °F 1 % 86,000 psi 4,400 cps - 26A:100B 20 min. 88 Metal Gray 4,400 cps 16 h. 20 min. 10,700 psi 86,000 psi 17.6 cu. in./lb. 1.57 g/cc 26A:100B 0.0006 in. / in. - 3,250 psi 1 % 88 149 °F 8,420 psi 514,000 psi 97,300 psi - - - - - - - - - -
TASK™ 21 1 h. 1.07 g/cc 25.9 cu. in./lb. 5,500 psi 270,000 psi 7,100 psi 78,500 psi 7,100 psi 0.0058 in. / in. 144 °F 7.5 % 250,000 psi 500 cps 2A:1B 2A:1B 6 min. 75 White 500 cps 1 h. 6 min. 7,100 psi 250,000 psi 25.9 cu. in./lb. 1.07 g/cc 2A:1B 0.0058 in. / in. 2A:1B 5,500 psi 7.5 % 75 144 °F 7,100 psi 270,000 psi 78,500 psi - - - - - - - - - -

Why buy at FormX?

Subscribe to our Newsletter

Receive €5,- discount on your first purchase!

Visa logo iDeal logo Mastercard logo Paypal logo FedEx logo FedEx logo
This website has been developed by Usecue B.V.
© 2026 FormX B.V.