TASK™ 2

Task2x ⓘ B80DD09C-DD3A-1C45-90A9-1A6D68097AA0
Polyurethane Resin

Low viscosity casting resin with high tensile and flexural strength.

  • Shore Hardness: 80 D
  • Mix Ratio: 1:1 by volume
  • Working time: 7 min
  • Cure Time: 60 min
  • Heat Deflection Temp: 57°C
exclamation.svg health-hazard.svg

Danger

H315 - Causes skin irritation.
H317 - May cause an allergic skin reaction.
H320 -
H332 - Harmful if inhaled.
H334 - May cause allergy or asthma symptoms or breathing difficulties if inhaled.
€ 171.06

(€ 141.37 without 21% VAT)

In stock

Description

This low viscosity, high-performance casting resin offers superior physical and performance properties. 

TASK™ 2 features a convenient 1:1 mix ratio by volume (115:100 by weight) and does not require vacuum degassing.

TASK™ 2 is white with high tensile and flexural strength, and a high flexural modulus. 

It is suitable for industrial applications such as pattern making and prototype model creation, and is designed for casting with thicknesses up to 1.27 cm (½ inch).

Technical Properties

  • Mix Ratio By Volume: 1:1
  • Mix Ratio By Weight: 115:100
  • Pot Life: 7 minutes
  • Cure Time: 60 minutes
  • Shore Hardness: 80 D
  • Specific Gravity: 1.12 g/cc
  • Specific Volume: 0.89 cm³/g
  • Color: White
  • Tensile Strength: 45.85 MPa
  • Elongation @ Break: 6%
  • Tensile Modulus: 2,000 MPa
  • Flexural Strength: 65.51 MPa
  • Flexural Modulus: 1,986 MPa
  • Compressive Strength: 57.23 MPa
  • Compressive Modulus: 538 MPa
  • Heat Deflection Temp: 57°C
  • Shrinkage: 0.005 mm/mm
  • Mixed Viscosity: 150 mPa·s (cps)

Instructions

Storage and Preparation

Store and use materials in a warm environment at 23°C. Use products as soon as possible due to limited shelf life. 

All liquid urethanes are moisture sensitive. Use clean mixing tools and metal, glass, or plastic containers. 

Mix in a well-ventilated area and wear safety glasses, long sleeves, and rubber gloves.

Release Agent Application

Test surface compatibility with a trial casting. Ensure polyurethane, latex, or metal molds are dry and apply a suitable release agent. Use a liberal coat of release agent, brush lightly, and follow with a light mist coating. Let dry for 30 minutes.

Measuring and Mixing

Mix ratio is 1:1 by volume or 115:100 by weight. Shake Part A & Part B before use. Dispense Part A into a mixing container, then add Part B. Mix thoroughly, scraping sides and bottom. Avoid splashing. Do not delay between mixing and pouring.

Pouring and Curing

Pour the mixture into the mold's lowest point. Use the pressure casting technique for the best results. Place the casting assembly in a pressure chamber at 4.2 kg/cm² for the full cure time. Ensure adequate ventilation and avoid inhaling fumes. 

Let the casting cool to room temperature before handling.

Post Curing

For maximum properties and heat resistance, post-cure by allowing full cure time at room temperature, followed by 4-8 hours at 65-72°C. Cool to room temperature before handling.

Safety and Handling

Fumes may appear during curing but will dissipate with ventilation. Castings may be extremely hot post-cure and can burn skin. Cool before handling. Wear a dust mask when machining cured plastics to prevent inhalation of particles.

Specifications

Color White
Mixed Viscocity 150 cps
Cure Time 60 minutes
Pot Life 7 minutes
Flexural Strength 9,500 psi
Flexural Modulus 288,000 psi
Specific Volume 24.7 cu. in./lb.
Specific Gravity 1.12 g/cc
Mix Ratio By Weight 115A:100B
Shrinkage 0.005 in. / in.
Mix Ratio By Volume 1A:1B
Tensile Strength 6,650 psi
Elongation At Break 6 %
Shore D Hardness 80
Heat Deflection Temp 134 °F
Compressive Strength 8,300 psi
Tensile Modulus 290,000 psi
Compressive Modulus 78,000 psi
Available in Polyurethane Resin
Product Cure Time Specific Gravity Specific Volume Tensile Strength Tensile Modulus Compressive Strength Compressive Modulus Flexural Strength Shrinkage Heat Deflection Temp Elongation At Break Flexural Modulus Mixed Viscocity Mix Ratio By Volume Mix Ratio By Weight Pot Life Shore D Hardness Color Mixed Viscocity Cure Time Pot Life Flexural Strength Flexural Modulus Specific Volume Specific Gravity Mix Ratio By Weight Shrinkage Mix Ratio By Volume Tensile Strength Elongation At Break Shore D Hardness Heat Deflection Temp Compressive Strength Tensile Modulus Compressive Modulus Handling Time Handling Time Heat Deflection With Post Cure Heat Deflection With Post Cure Shore A Hardness Die C Tear Strength Hundred Percent Modulus Hundred Percent Modulus Die C Tear Strength Shore A Hardness
TASK™ 2 60 min. 1.12 g/cc 24.7 cu. in./lb. 6,650 psi 290,000 psi 8,300 psi 78,000 psi 9,500 psi 0.005 in. / in. 134 °F 6 % 288,000 psi 150 cps 1A:1B 115A:100B 7 min. 80 White 150 cps 60 min. 7 min. 9,500 psi 288,000 psi 24.7 cu. in./lb. 1.12 g/cc 115A:100B 0.005 in. / in. 1A:1B 6,650 psi 6 % 80 134 °F 8,300 psi 290,000 psi 78,000 psi - - - - - - - - - -
TASK™ 3 90 min. 1.12 g/cc 24.7 cu. in./lb. 6,650 psi 290,000 psi 8,300 psi 78,000 psi 9,500 psi 0.0025 in. / in. 134 °F 6 % 288,000 psi 150 cps 1A:1B 115A:100B 20 min. 80 White 150 cps 90 min. 20 min. 9,500 psi 288,000 psi 24.7 cu. in./lb. 1.12 g/cc 115A:100B 0.0025 in. / in. 1A:1B 6,650 psi 6 % 80 134 °F 8,300 psi 290,000 psi 78,000 psi - - - - - - - - - -
TASK™ 4 16 h. 1.167 g/cc 23.9 cu. in./lb. 6,500 psi 130,000 psi 7,400 psi 75,000 psi 9,000 psi 0.0035 in. / in. 110 °F 4 % 204,000 psi 250 cps - 100A:100B 20 min. 83 Ivory 250 cps 16 h. 20 min. 9,000 psi 204,000 psi 23.9 cu. in./lb. 1.167 g/cc 100A:100B 0.0035 in. / in. - 6,500 psi 4 % 83 110 °F 7,400 psi 130,000 psi 75,000 psi - - - - - - - - - -
TASK™ 5 24 h. 1.1 g/cc 25.2 cu. in./lb. 4,530 psi 200,000 psi 6,700 psi 83,000 psi 6,480 psi 0.007 in. / in. 145 °F 5 % 216,000 psi 600 cps 1A:1B 1A:1B 3 min. 77 Tan 600 cps 24 h. 3 min. 6,480 psi 216,000 psi 25.2 cu. in./lb. 1.1 g/cc 1A:1B 0.007 in. / in. 1A:1B 4,530 psi 5 % 77 145 °F 6,700 psi 200,000 psi 83,000 psi 15 min. 15 min. - - - - - - - -
TASK™ 6 24 h. 1.07 g/cc 25.9 cu. in./lb. 5,200 psi 146,000 psi 5,570 psi 65,000 psi 6,200 psi 0.0031 in. / in. 162 °F 4 % 182,500 psi 800 cps 1A:1B 1A:1B 7 min. 75 Tan 800 cps 24 h. 7 min. 6,200 psi 182,500 psi 25.9 cu. in./lb. 1.07 g/cc 1A:1B 0.0031 in. / in. 1A:1B 5,200 psi 4 % 75 162 °F 5,570 psi 146,000 psi 65,000 psi 75 min. 75 min. - - - - - - - -
TASK™ 7 10 min. 1.2 g/cc 23.1 cu. in./lb. 3,390 psi 150,700 psi 5,140 psi 57,600 psi 5,450 psi 0.0111 in. / in. 131 °F 15.1 % 148,900 psi 200 cps 1A:1B 104A:100B 2.5 min. 73 Off-White 200 cps 10 min. 2.5 min. 5,450 psi 148,900 psi 23.1 cu. in./lb. 1.2 g/cc 104A:100B 0.0111 in. / in. 1A:1B 3,390 psi 15.1 % 73 131 °F 5,140 psi 150,700 psi 57,600 psi - - - - - - - - - -
TASK™ 8 15 min. 1.09 g/cc 25.4 cu. in./lb. 5,840 psi 246,000 psi 8,760 psi 77,400 psi 8,280 psi 0.01 in. / in. 194 °F 4 % 271,000 psi 100 cps 1A:1B 120A:100B 2.5 min. 80 Off-White 100 cps 15 min. 2.5 min. 8,280 psi 271,000 psi 25.4 cu. in./lb. 1.09 g/cc 120A:100B 0.01 in. / in. 1A:1B 5,840 psi 4 % 80 194 °F 8,760 psi 246,000 psi 77,400 psi - - 263 °F 263 °F - - - - - -
TASK™ 11 16 h. 1.12 g/cc 24.7 cu. in./lb. 2,500 psi - - - - 0.0024 in. / in. - 100 % - 2,000 cps - 100A:100B 20 min. 60 Translucent White 2,000 cps 16 h. 20 min. - - 24.7 cu. in./lb. 1.12 g/cc 100A:100B 0.0024 in. / in. - 2,500 psi 100 % 60 - - - - - - - - - - - - - -
TASK™ 12 16 h. 1.08 g/cc 26 cu. in./lb. 2,700 psi - - - - 0.001 in. / in. - 300 % - 2,400 cps - 100A:44B 20 min. 60 Clear Amber 2,400 cps 16 h. 20 min. - - 26 cu. in./lb. 1.08 g/cc 100A:44B 0.001 in. / in. - 2,700 psi 300 % 60 - - - - - - - - - - - - - -
TASK™ 13 20 min. 1.15 g/cc 24.1 cu. in./lb. 1,800 psi - - - - 0.005 in. / in. - 125 % - 800 cps - 100A:120B 3 min. 50 Black 800 cps 20 min. 3 min. - - 24.1 cu. in./lb. 1.15 g/cc 100A:120B 0.005 in. / in. - 1,800 psi 125 % 50 - - - - - - - - - - - - - -
TASK™ 14 45 min. 1.15 g/cc 24.1 cu. in./lb. 1,800 psi - - - - 0.0035 in. / in. - 125 % - 800 cps - 100A:120B 10 min. 50 Black 800 cps 45 min. 10 min. - - 24.1 cu. in./lb. 1.15 g/cc 100A:120B 0.0035 in. / in. - 1,800 psi 125 % 50 - - - - - - - - - - - - - -
TASK™ 15 1 h. 1.12 g/cc 24.7 cu. in./lb. 2,720 psi 126,000 psi 5,450 psi 60,000 psi 5,450 psi 0.0042 in. / in. 117 °F 20 % 170,000 psi 600 cps - 75A:100B 6 min. 75 Opaque White 600 cps 1 h. 6 min. 5,450 psi 170,000 psi 24.7 cu. in./lb. 1.12 g/cc 75A:100B 0.0042 in. / in. - 2,720 psi 20 % 75 117 °F 5,450 psi 126,000 psi 60,000 psi - - - - - - - - - -
TASK™ 16 24 h. 1.08 g/cc 25.64 cu. in./lb. 2,264 psi - - - - 0.0025 in. / in. - 233 % - 1,400 cps - 1A:2B 6 min. 30 Light Yellow 1,400 cps 24 h. 6 min. - - 25.64 cu. in./lb. 1.08 g/cc 1A:2B 0.0025 in. / in. - 2,264 psi 233 % 30 - - - - 90 min. 90 min. - - 80 197 pli 855 psi 855 psi 197 pli 80
TASK™ 18 16 h. 1.57 g/cc 17.6 cu. in./lb. 3,250 psi 514,000 psi 8,420 psi 97,300 psi 10,700 psi 0.0006 in. / in. 149 °F 1 % 86,000 psi 4,400 cps - 26A:100B 20 min. 88 Metal Gray 4,400 cps 16 h. 20 min. 10,700 psi 86,000 psi 17.6 cu. in./lb. 1.57 g/cc 26A:100B 0.0006 in. / in. - 3,250 psi 1 % 88 149 °F 8,420 psi 514,000 psi 97,300 psi - - - - - - - - - -
TASK™ 21 1 h. 1.07 g/cc 25.9 cu. in./lb. 5,500 psi 270,000 psi 7,100 psi 78,500 psi 7,100 psi 0.0058 in. / in. 144 °F 7.5 % 250,000 psi 500 cps 2A:1B 2A:1B 6 min. 75 White 500 cps 1 h. 6 min. 7,100 psi 250,000 psi 25.9 cu. in./lb. 1.07 g/cc 2A:1B 0.0058 in. / in. 2A:1B 5,500 psi 7.5 % 75 144 °F 7,100 psi 270,000 psi 78,500 psi - - - - - - - - - -

Why buy at FormX?

Subscribe to our Newsletter

Receive €5,- discount on your first purchase!

Visa logo iDeal logo Mastercard logo Paypal logo FedEx logo FedEx logo
This website has been developed by Usecue B.V.
© 2026 FormX B.V.