Shell Shock™ SLOW

ShellshockSlowx ⓘ CEBC4ADE-AD94-4446-9D44-08B76BC33750
Polyurethane Resin

Thixotropic epoxy coating for hard, impact-resistant shells that thickens upon mixing and can be brushed without sagging. Slow version

  • Mix ratio: 1A:4B by weight
  • Working time: 10 minutes
  • Demold time: 16 hours
  • Compatible with foam, wood, and other surfaces
exclamation.svg health-hazard.svg

Danger

H315 - Causes skin irritation.
H317 - May cause an allergic skin reaction.
H320 -
H332 - Harmful if inhaled.
H334 - May cause allergy or asthma symptoms or breathing difficulties if inhaled.
€ 136.85

(€ 113.10 without 21% VAT)

Out of stock

Description

This thixotropic epoxy coating is designed for creating hard, impact-resistant shells. It is suitable for coating foam, wood, and other surfaces.
This product material cures at room temperature with virtually no shrinkage to a hard, durable plastic that exhibits good compressive and flexural strength. Fully cured castings are rigid and can be sanded, primed, and painted. Color effects can be achieved by adding SO-Strong™ Color Tints.

Features

  • Mix ratio: 1A:4B by weight
  • Pot life: 10 minutes
  • Demold time: 16 hours
  • Compatible with foam, wood, and other surfaces
  • Once cured, the coating provides a durable, high-impact surface that can be sanded, primed, and painted.

Instructions

  • Mix epoxy at a ratio of 1A:4B by weight until uniform. 
  • Apply to clean, dry surfaces using a brush or tool. 
  • Working time is approximately 10 minutes. 
  • Apply in even layers; do not overwork. 
  • Allow to cure undisturbed. 
  • Demold or handle after approximately 16 hours. 
  • Once cured, the surface can be sanded, primed, or painted. 
  • Wear gloves and ensure proper ventilation.

Specifications

Color Beige
Mixed Viscocity 3,000 cps
Cure Time 5 hours
Pot Life 8 minutes
Flexural Strength 7,150 psi
Flexural Modulus 980,000 psi
Specific Volume 17.3 cu. in./lb.
Specific Gravity 1.60 g/cc
Mix Ratio By Weight 1A:5B
Shrinkage 0.0006 in. / in.
Mix Ratio By Volume 1A:4B
Tensile Strength 3,100 psi
Elongation At Break 0.4 %
Shore D Hardness 85
Heat Deflection Temp 135 °F
Compressive Strength 9,000 psi
Tensile Modulus 435,000 psi
Compressive Modulus 500,000 psi
Available in Polyurethane Resin
Product Cure Time Specific Gravity Specific Volume Tensile Strength Tensile Modulus Compressive Strength Compressive Modulus Flexural Strength Shrinkage Heat Deflection Temp Elongation At Break Flexural Modulus Mixed Viscocity Mix Ratio By Volume Mix Ratio By Weight Pot Life Shore D Hardness Color Mixed Viscocity Cure Time Pot Life Flexural Strength Flexural Modulus Specific Volume Specific Gravity Mix Ratio By Weight Shrinkage Mix Ratio By Volume Tensile Strength Elongation At Break Shore D Hardness Heat Deflection Temp Compressive Strength Tensile Modulus Compressive Modulus
Shell Shock™ FAST 60 min. 1.60 g/cc 17.3 cu. in./lb. 3,100 psi 435,000 psi 9,000 psi 500,000 psi 7,150 psi 0.0006 in. / in. 135 °F 0.4 % 980,000 psi 3,000 cps 1A:4B 1A:5B 3 min. 85 Beige 3,000 cps 60 min. 3 min. 7,150 psi 980,000 psi 17.3 cu. in./lb. 1.60 g/cc 1A:5B 0.0006 in. / in. 1A:4B 3,100 psi 0.4 % 85 135 °F 9,000 psi 435,000 psi 500,000 psi
Shell Shock™ SLOW 5 h. 1.60 g/cc 17.3 cu. in./lb. 3,100 psi 435,000 psi 9,000 psi 500,000 psi 7,150 psi 0.0006 in. / in. 135 °F 0.4 % 980,000 psi 3,000 cps 1A:4B 1A:5B 8 min. 85 Beige 3,000 cps 5 h. 8 min. 7,150 psi 980,000 psi 17.3 cu. in./lb. 1.60 g/cc 1A:5B 0.0006 in. / in. 1A:4B 3,100 psi 0.4 % 85 135 °F 9,000 psi 435,000 psi 500,000 psi

Why buy at FormX?

Subscribe to our Newsletter

Receive €5,- discount on your first purchase!

Visa logo iDeal logo Mastercard logo Paypal logo FedEx logo FedEx logo
This website has been developed by Usecue B.V.
© 2026 FormX B.V.